| Place of Origin: | China |
|---|---|
| Brand Name: | CRYLINK |
| Certification: | Iso9001 |
| Model Number: | CRYLINK-LiF Crystal |
| Minimum Order Quantity: | 1 Pieces |
| Price: | negotiation |
| Packaging Details: | Carton |
| Delivery Time: | 3-4 weeks |
| Payment Terms: | TT |
| Supply Ability: | 100 pieces /month |
| Name: | LiF Optical Crystals | Density, G/cm3: | 2.64 |
|---|---|---|---|
| Melting Point,℃: | 870 | Transmission Range, M: | 0.12-6 |
| High Light: | LiF Lithium Flouride Crystals,LiF Optical Crystals,2.64g/cm3 LiF Crystals |
||
Product Details
Description
LiF (Lithium Flouride) crystals shows excellent transmittance in the VUV region. It is used for windows, prisms, and lenses in the visible and infrared in 0.104 m - 7 m. LiF crystalis sensitive to thermal shock and would be attacked by atmospheric moisture at 400°C. In addition irradiation produces color centers.
Modest precautions should be taken against moisture and high energy radiation damage. Besides LiF is softens at 600°C and is slightly plastic that can be bent into radius plates. The material can be cleaved along (100) and less commonly (110). Although the optical characteristics are good the structure is not perfect and cleavage is difficult.
High quality LiF is usually grown by modified Bridgman technique.
Lithium Flouride shows good optical properites. It can be used for windows, prisms and lenses in the vacuum UV,visibel and infrared. Because of its paricular lattice structure, LiF can also be used as X-ray diffraction devices.
Features:
Excellent Transmission from 110nm to 7m;
Optically isotropic, middle hard;
Hygroscopic, unsolvable in water;
Sensitive to thermal shock,Cleaved along (100);
Specification
|
Physical Properties |
|
|
Crystal type |
cubic |
|
Lattice constant, |
a=4.026 |
|
Density, g/cm3 |
2.64 |
|
Melting point,℃ |
870 |
|
Refractive index @ 1.0m |
n=1.387 |
|
Transmission range, m |
0.12-6 |
|
Specifications for LiF windows |
|
|
Spectal range |
UV, VIS, IR |
|
Surface quality |
60-40 S & D |
|
Clear aperture |
90% of the diameter |
|
diameter tolerance |
+0, -0.1 mm |
|
Thickness tolerance |
±0.1 |
|
Surface flatness |
/4 @ 633 nm |
|
parallelism |
<3 arcmin |
|
Polishing Specification for Optical GradeⅠ |
|
|
Orientation Tolerence |
< 1° |
|
Thickness/Diameter Tolerance |
±0.10 mm |
|
Surface Flatness |
<(-2)@632nm |
|
Wavefront Distortion |
<(2-4)@632nm |
|
Surface Quality |
80/50 |
|
Parallel |
10 |
|
Perpendicular |
60 |
|
Clear Aperture |
>90% |
|
Chammfer |
<0.2×45° |
|
Polishing Specification for Optical Grade Ⅱ |
|
|
Orientation Tolerence |
< 0.5° |
|
Thickness/Diameter Tolerance |
±0.10 mm |
|
Surface Flatness |
<(/2-/4)@632nm |
|
Wavefront Distortion |
<(1-2)@632nm |
|
Surface Quality |
60/40 |
|
Parallel |
1 |
|
Perpendicular |
30 |
|
Clear Aperture |
>90% |
|
Chammfer |
<0.2×45° |